PrimaCreator Value Flex photopolymer resin is designed for detailed prints with high impact resistance. Printed objects are flexible, with an elongation at break of 130% and low shrinkage. The resin is optimized for 395–405 nm UV light sources and works with low-power DLP printers.

Curing time is 4–12 seconds per 0.05 mm layer, while the first layer requires 40–60 seconds. After printing, clean the object with isopropyl alcohol (IPA). For final curing, allow approximately 2–5 minutes in a UV chamber, 10–20 minutes in direct sunlight, or up to 60 minutes in cloudy daylight.

• Resin type: Flexible
• Color: Light gray
• Capacity: 500 ml
• Compatibility: PrimaCreator
• UV wavelength: 395–405 nm
• Shore D hardness: 65–75
• Elongation at break: 130%
• Flexural strength: 40–70 MPa
• Flexural modulus: 1.882–2.385 MPa
• Tensile strength: 30–52 MPa
• Tensile modulus: 1.779–2.385 MPa
• Notched impact strength: 41–48 J/m
• Heat deflection temperature: 80 ℃
• Glass transition temperature: 100 ℃
• Thermal expansion: 95*E-6
• Volumetric shrinkage: 3,72–4,24%
• Linear shrinkage: 1,05–1,35%
• Density: 1,05–1,25 g/cm³
• Viscosity: 150–300 MPa·s
• Curing time per layer: 4–12 seconds for a layer thickness of 0.05 mm
• First-layer curing time: 40–60 seconds