Anycubic ABS-Like Resin Pro 2 is designed for printing models and parts that require tensile, flexural and impact strength, along with increased flexibility. Elongation at break reaches 35–40%, while volumetric shrinkage is 4.3–5.6%, helping reproduce fine details and produce smooth finished models. Its formulation reduces odour during printing.

Its low viscosity and good flow make printing easier, while adhesion to the build plate helps reduce print failures. It is compatible with LCD and DLP printers that use UV radiation with a wavelength of 365–405 nm and is optimised for Anycubic LCD printers.

• Resin type: ABS-like photopolymer
• Colour: Grey
• Compatibility: LCD and DLP printers with 365–405 nm UV radiation; Anycubic LCD printers
• Viscosity: 300–400 mPa·s at 25 °C
• Density: 1.05–1.25 g/cm³
• Hardness: 82–84 HD
• Tensile strength: 35–45 MPa
• Elongation at break: 35–40%
• Flexural modulus: 40–45 MPa
• Flexural strength: 1400–1800 MPa
• Young’s modulus: 1,600–1,800 MPa
• Izod impact strength: 212 J/m
• Volumetric shrinkage: 4.3–5.6%
• Printing temperature: 20–50 °C
• Ambient printing temperature: 20–40 °C
• First-layer exposure time: 20–40 s
• Standard-layer exposure time: 1.5–3 s
• Cleaning agent: 95% IPA
• Washing time: At least 3 minutes
• UV wavelength during curing: 405 nm
• Curing temperature: 18–30 °C
• UV intensity: 25,000–30,000 μW/cm²
• Curing time: 3 minutes
• Weight: 1 kg